703 Epoxy iron workshop primer
[ Back ]
Details

Composition of a two-component epoxy ferrite vehicle made of iron oxide, epoxy resin, polyamide curing agent, etc..
The primer.
The main characteristics have good anti-rust performance. When the film thickness is 25 μm, the maintenance period is 3-6 months. The paint film does not contain zinc and does not produce harmful gas when welding and cutting; Dry fast, can be moved, stacked and painted in a short period of time; It has excellent welding and cutting properties, and the thickness of the paint film is within the prescribed range, which does not affect the welding and cutting performance. Excellent adhesion and impact resistance; Good oil resistance, water resistance and solvent resistance; Can be matched with most of the paint system; Recognized by the China Classification Society.
Used for pretreatment pipelines such as shipyards, heavy machinery plants, and steel structure factories for workshop primers. The maintenance period is approximately 3-6 months.
Appearance iron red, no light
Construction parameter volume solid mass 28 x 3 %(as specified in GB / T9272 eqv IS 03233:1998)(after mixing)
Ratio A: Part B = 5:2(weight ratio)
Dry film thickness 25 μm
Wet film thickness 89 μm
Theoretical dosage 102g/m2
Flash point A component(base) 5 °C; Part B(curing agent) 5 °C
Ripening time(mixed)(25 °C) 30 min
Dry time(25 °C) surface dry ≤ 5 min; Dry ≤ 24h; Complete curing 7D; Pipeline drying time(steel Preheat 50 °C, oven temperature 120 °C) ≤ 5 min
Coating interval
Temperature 5 °C 20 °C 30 °C
Shortest 24h16h8h
Maximum unlimited
Available Time(after mixing A and B)
Temperature 5 °C 20 °C 30 °C
Available 24h8h6h
It is recommended that the number of coating channels be 1 and the thickness of the dry film be 25 μm.
Application of posterior coating to coating systems such as chlorinated rubber, epoxy, epoxy asphalt, asphalt system, epoxy Ester, phenolic, alkyd etc..
Surface treatment of steel paste sand treatment to Sa2. Level 5, surface roughness 30-75 μm
The temperature of the substrate under construction conditions must be higher than 3 °C above the dew point; When the temperature is below 5 °C, the curing reaction between epoxy and curing agent stops, and it is not suitable for outdoor construction. Relative humidity not more than 85 %
The coating method has no air spray thinner 106 thinner; Dilution 0-10 %(in paint quantity); The nozzle diameter is 0.4-0 .5 mm; Ejection pressure 15 MPa(approximately 150 kg/cm2)
Air spray thinner 106 thinner; Dilution 0-10 %(by paint weight); Nozzle diameter 2.0-2 .5 mm; Air pressure 0.3-0 .6 MPa(3-6 kg/cm2)
Rolling / Brush is limited to small area repair; diluent 106 diluents; Dilution 0-3 %(by paint weight)
Cleaning agent 103 diluent
Safety measures refer to the product safety technical specifications of Zhongsheng Paint(Ningbo) Co., Ltd..
Packaging component A(base) 20L barrel 16kg
Part B(curing agent) 10 L barrel 6.4 kg
Warranty period 12 months
Remark for the correct use of our products, please carefully read this manual "use guidelines."
Declare that the above information and data are based on our experience in testing and practical use and can be used as a construction guide. We are only responsible for the quality of the paint itself for the construction that we do not understand. We shall have the right to modify this instruction according to the continuous improvement of the product.